Первичные переработанные гранулы HIPS полистирол смола модель

Performance of Projects

Test Method

Test Data

Data Unit

MFI (200°C/5KG)

ASTM D-1238

4.5

G/10min

Vicat Softening Point

ASTM D-1525

94 Min

°C

Tensile Strength at Break

ASTM D-638

20

MPa

Tensile Strength at Yield

ASTM D-638

21

MPa

Elongaion at Break

ASTM D-638

55

g

Tensile Modulus

ASTM D-638

1800

MPa

Flexural Modulus

ASTM D-790

1750

MPa

Izod Impact

ISO 180/1A

8.5 Min

%

Water Absorption

ASTM D-570

0.1 Max

%