Заводская Цена огнестойкие пластиковые

Properties

Test Method

Test Condition

Units

Typical Values

Physical

Melt Flow Rate  

ISO1133

230℃, 2.16Kg

g/10min

--

Specific Gravity  

ISO1183

23℃

g/cm3

0.9

Ash  

ISO3451

800℃,30min

%

0

Mechanical

Tensile Strength

ISO527

50mm/min

MPa

35

Elongation at Yield

ISO527

50mm/min

%

8

Flexural Strength  

ISO178

2mm/min

MPa

--

Flexural Modulus  

ISO178

2mm/min

MPa

1731

Impact Strength, IZOD non-notched

ISO179/1eU

23℃

KJ/m2

NB

-30℃

KJ/m2

-

Impact Strength, IZOD notched

ISO179/1eA

23℃

KJ/m2

2.8

-30℃

KJ/m2

-

Thermal

Heat Deflection Temp.  

ISO75/B

0.45MPa

℃

97

ISO75/A

1.8MPa

℃

-

Melting Point

DSC

℃

164

Vicat softness point

ISO306

℃

115

Others

Shore Hardness

ISO2039

-

N/mm2

--

Mold Shrinkage

-

23℃

Flammability  

TL1010

-

mm/min