HIPS 8250 | Test Condition | Test Method | Value | Unit | ||||
Basic Properties | ||||||||
Density | ASTM D792 | 1.04 | g/cm³ | |||||
Melt Flow Index | 230℃/2.16kg | ASTM D1238 | 5.5 | g/10min | ||||
Mechanical Performance | ||||||||
Tensile Modulus | 23°C | ASTM D638 | 2160 | MPa | ||||
Tensile Strength | 23°C | ASTM D638 | 23 | MPa | ||||
Elongation | 23°C | ASTM D638 | 53 | % | ||||
Flexural Strength | 23°C | ASTM D790 | 45 | MPa | ||||
Flexural Modulus | 23°C | ASTM D790 | 2260 | MPa | ||||
Izod Notch Impact | 23°C 6.4mm | ASTM D256 | 124 | J/m | ||||
Thermal Performance | ||||||||
H.D.T | Annealed 3.2mm at 80°C for 2 hours | ASTM D648 | 89 | °C | ||||
Vicat | Annealed 3.2mm at 80°C for 2 hours | ASTM D1525 | 101 | °C |