![]() Play a critical role in the integrity of concrete structures. They provide a fluid tight diaphragm when embedded in and running through concrete joints.
PVC Waterstop seal by Jaypee Profile greatly expands the scope of conventional waterstop by offering unmatched resistance to broad spectrum of ozone, oxygen, alkalies & aqueous borne chemicals. We are known worldwide for our high quality waterstops from high grade PVC resin extrusions that are plasticised and stablised to offer long life.
Product Data
Storage/Shelf Life : 60 months from date of production if stored in unopened, undamaged and sealed original packaging, in dry conditions at temperatures not exceeding +30°C. Protect from UV light.
Color : White, Grey, Orange as per the requirement.
Chemical Resistance Permanent : Water, seawater, sewage, road salt solutions.
Temporarily : Diluted inorganic alkalis, mineral acids and mineral oils.
Structure That Require Water Stop
- Storage Tanks.
- Retaining Walls.
- Swimming Pools.
- Water & Waste Water Treatment Plants.
- Subways, Tunnels & Culverts.
- Dams, Canals & Water Reservoirs.
- Foundation, Basements, Underground Parkings.
- Pumping Stations, Underground Chambers.
- Drainage and Sewerage Concrete structures (Sewerage Treatment Plants).
| STOP TYPE | SECTION | WIDTH MM | THICKNESS MM | SAFE-HYDRAULIC PRESSURE MTRS | DESCRIPTION AND STABILITY | | 150 B | ![]() | 150 | 4 to 5 | 25 | For low hydro-static heads, used in exp./contraction joints. | | 150 AU | ![]() | 150 | 6 | 32 | For moderate pressure in RCC wall or slab, wall/slap not less thicker than 150 mm. | | 150 A | ![]() | 180 | 8 to 11 | 40 | For high hydro-static heads, in expansion/contraction joints. | | 180 X E | ![]() | 230 | 10 | 45 | For High Expansion/contraction and where differential settlement is expected. | | 230 G | ![]() | 230 | 4 to 5 | 30 | For medium pressure head and wall not less thicker than 230 mm. | | 230 GU | ![]() | 230 | 6 | 36 | For medium pressure heads, for construction and expansion/contraction joints. | | 225/230D | ![]() | 225/230 | 8 to 11 | 50 | For High heads, utility same as 230 GU. | | 230 KE | ![]() | 230 | 5 | 25 | Surface type, for expansion/contraction joints. | | 230 KD | ![]() | 230 | 5 | 25 | For constrution joints, externally placed type of PVC waterstop. | | 240 RS | ![]() | 240 | 5 | 25 | Multi Ribs and serrations. Ideal waterstop for construction joints. | | 240 H | ![]() | 240 | 8 to 10 | 42 | For moderate to high pressure heads used in Power Houses & other important RCC structures. | | 230 XA | ![]() | 230 | 10 | 40 | For high expansion/contraction & settlement joints. | | 230 XB | ![]() | 230 | 5 | 25 | For medium pressure, utility same as 230 XA. | | 300 LU | ![]() | 300 | 6 | 35 | Multi Ribbed and serrated, Ideal watrestop for underground structures, in expansion/contraction joints. | | 300 LUNB | ![]() | 300 | 6 | 35 | Ditto as above but without central bulb for construction joints. | | 300 N | ![]() | 300 | 10 | 52 | As per IS 12200 of 1987. Sketch shown, in the Dams, syphons, Aqueducts etc. | | 305 F | ![]() | 305 | 9 to 12 | 60 | A standard design of CWC for Dams & other Hydraulic structures with high pressure heads. | | 320 KY | ![]() | 320 | 5 | 30 | Surface type with wooden crack inducer, but same as 320 KZ. | | 320 KZ | ![]() | 320 | 5 | 30 | Surface type, without crack inducer, used for construction joints, approved design of CPWD. | | 150 XX | ![]() | 150 | 5 | 20 | Dumb-bell type, with double central bulb specially developed for Larson & Tourbo ECC construction group. | | 150 IS | ![]() | 150 | 7.5 | 35 | Replaceable without central bulb. | | 300 IS | ![]() | 300 | 10 | 50 | Replaceable type with a trapezoidal central bulb protruded on the same face where semi circular solid end bulbs are projected to ensure basic grip. |
Technical Specification PVC Water Stop Seal
As per IS:15058
| Sl. No | Characters | Unit | Specification | | 1 | Tensile Strength | Mpa | 13.8 Min. | | 2 | Elongation at Break | % | 285 Min. | | 3 | Hardness | Shore-A | 65 Min. | | 4 | Water Absorption | % | 00.6 Max. | | 5 | Cold Resistance (at – 25C) | Visual | No Crack | | 6 | Accelerated ExtractionTest | | A. | Tensile Strength | Mpa | 10.3 Min. | | B. | Elongation at Break | % | 280 Min. | | 7. | Stability in effect of Alkalies test. | | A. | Weight increase at 7 days | % | 0.25 Max. | | B. | Weight decrease at 7 days | % | 0.10 Max. | | C. | Change in hardness at 7 days | Shore-A | +-5 | | D. | Weight increase at 28 days | % | 0.40 Max. | | E. | Weight decrease at 28 days | % | 0.30 Max | | F. | Dimension Change | % | +-1 |
As per British standard BS 2571:1990
| PROPERTY | METHOD 2782 | SPECIFICATION | RESULT | | Softness | 365A | 30 –50 (A77 +/-5) | 45 (A74) | | Tensile Strength, MPa | 320A | 14 (min) | 14.3 | | Elongation, % | 320A | 250 (min) | 435 | | Plasticizer Loss on | 465B | 2.0 (max) | 0.5 | | Heating, % | - | - | - | | Cold Bend Temp, °C | 151A | -25(max) | -45 | | Cold Flex Temp, °C | 150B | -5 (max) | -32 |
As per ANSI Standards
| PHYSICAL PROPERTIES | TEST METHOD | PREMIUM GRADE | | Tensile Strength | ASTM D 638 Type IV | 13 MPa | | Ultimate Elongation | ASTM D 638 Type IV | 340% | | Low Temp. Brittleness | ASTM D 746 | -38° C (-37° F) | | Tear Resistance | ASTM D 624 Die “B” | 50 kn/m | | Modulus of Elasticity | ASTM D 638 Type IV | 10 MPa | | Effects of Alkali | ASTM D 471 CGSB | 4.5% | | Change in mass | 41-GP-34M | -td> | | Ultimate Elongation | ASTM D 471 CGSB | 280%
|
|