Керамическое высокотемпературное антикоррозийное защитное покрытие на керамической водонепроницаемой

 High humidity, high temperature or high acid concentration environment is always be a difficult problem for anticorrosion coatings, some material improved its anticorrosion property, but it becomes more fragile which can not meet the requirements of huge steel structure or concrete surface. SWD ceramic coating combines inorganic SiO2 which has strong anticorrosion and temperature variation resistance with organic compound. It is two components polyfunctionality, solvent free coating, the cured film has high crosslinking density, there is no hydroxyl and ester in the molecular chain structure but strong chemical bond ester bond (C-O-C). So the anticorrosion performance is excellent.

Characteristics             

Ceramic coating can resist any high acid, alkali and other solvents, the coating film is compact and strong that can withstand the cyclic stress damage of steel structure and small cracks of concrete surface, with excellent adhesive strength on various metal or non metallic materials, high heat resistant and temperature shock resistance. Impact and collision resistance and abrasion resistance. Anti-UV and weather that can be long-term applied outdoor. Ceramic coating is solvent free, eco friendly, high hardness and good flexibility, it will not peel off or crack after long term use. Several types available for different corrosion environment conditions.  

SWD860 ceramic coating anticorrosive media table  

Specifications 

Adhesive strength (steel sheet substrate)          26Mpa 

Heat resistance 250℃,4 hour                               No cracking, no delamination, no soften or yellow 

Temperature variation resistance (alternating 240℃  

and cold water 30 minutes/ time for30 times)    no crack, no bubbles, no soften. 

Surface Hardness                                                  4H~8H 

Abrasion resistance(750g/500r)                        4mg 

Slat spray resistance 2000h   No corrosion, no bubbles no peeling                                                                        

 Data of Performance

 Color                                                        Multiple colors as customers’needs 

Gloss                                                       gloss 

Specific Gravity                                      1.4~1.6g/cm3 

Volume solids content                            99%±1% 

VOC                                                            0 

Recommended dry film thickness         250~500μm 

Theoretical coverage                          0.4 kg/m2(calculated by the above solids percentage and dry film thickness of 250um) 

Practical coverage                              Allow appropriate loss rate 

Overcoating interval                             Min:2 hours, Max: 24 hours 

Application method                              Scraper or airless spray(import or domestic)

 Flash Point                                          180℃

Recommended procedures

Application scope           high acid, alkali or solvent corrosion environment, protection for equipment, steel structure, floor, water pool, storage tanks in high humidity environment of chemical, oil refining, power generation, metallurgy industry.

Shelf life                   at least 12 months (indoor with dry and cool conditions)

Packing: 25L steel drum