YL-PL-SR is polycarboxylate ether based high performance copolymer designed for highest concrete quality. It enables concrete to be produced highly workable at low dosage with improved slump retention. Compared to traditional Superplasticizer, YL-PL- SR has higher water  reduction, long slump retention, and higher early strength than others.

 

YL-PL-SR is a neutral concentrate grade, and mainly used as a raw material to produce different types of high performance water reducers for targeted industrial. It complies with ASTM C494, Type F specifications.

 

1. YL-PL-SR can be applied in a wide variety industry and can improve the workability to the concrete and to improve  high early  compressive strength, even with  low water/cement ratio while maintaining normal levels of workablility. Higher slump retention applications for high strength concrete.

 

2. It can be widely used in conventional concrete, pumping concrete, super-fluid self-compacting and high-performance concrete; it has the excellent performance especially in the application of high-strength high performance concrete.

 

1. Improve slump retention time in concrete. 

2. Effect long distance transportation for a long period of time. 

3. Reduce slump loss and improve workability. 

4. Decrease bleeding of materials separation. 

5. High water reducing rate and excellent plasticizing effect. Produces concrete with high levels of workability without segregation. 

6. Excellent dispersion and self-compacting effect can produce different grade strength 

super fluid self-compacting concrete. 

7. Can be a substantial increase in early and late strengths of concrete, so that increase the project construction schedule. 

8. Better plasticity-maintaining could significantly prolong the transit time of concrete, 

it reduce economic losses and ensure the normal pumping of concrete. 

9. Improves the frost resistance and carbonation resistance of the concrete. Lower drying shrinkage of the concrete by 20% or more compared with naphthalene-based admixtures. 

10. High applicability: It can be used with different variety of cement. 

11. Improved finished concrete surface ability. 

12. Proffer air environment protect. 

13. No chloride ions and no corrosion to steel bar. 

 

Items	Specification
Appearance	Light Brown Liquid
Solid Content (%)	50%±2.0
Density (23℃)(kg/m3)	1.16±0.05
Chloride Content (%)	≤0.10
Na2SO4Content (%)	≤4.0
Na2O+0.658K2O (%)	≤5.0
Solubility	Excellent
Cement Paste Flow	≥240

 

 

Items		Specification
Water Reducing Rate %		≥25
Compressive Strength Ratio %	1 day	≥170
	3 days	≥160
	7 days	≥150
	28 days	≥140
Air Content %		≤2.5
Bleeding Ratio %		≤50
Shrinkage Ratio (28 day) %		≤110
Setting Time difference min.	Initial	-90~+120
	Finally
Chloride Penetration coulomb		≤2000
F/T Cycles, Time		≥200
Slump Retention (60min) mm		≥150

 

The usual dosage of this product is 0.2-0.5% of the weight of cementing material. (dilute to 20% solid content)

 

200 kg IBC drums, 1.1 ton IBC tank, flexible tank. The ideal storage temperature is 5-40°C, avoid sun, rain, and freezing.

Once freeze, it can be used after melting and mixing. The self life is 6 months in original tightly closed drums.

 

After setting aside for long time (over one month), please fully mix before using.