High Temperature Resistant Type-SWANCOR 907 Series
SWANCOR 907 Series combines superior retention of mechanical properties at high temperature, such as tensile and flexural strength, and superior corrosion to chemical mixture, oxidizing chemicals and solvents etc.
Features
* Superier toughness.
* Excellent fatigue resistance.
* Premium performance at elevated temperature.
* Compliance with US FDA regulation 21 CFR 177.2420.
Products
SWANCOR 907-1 | Temperature resistance up to 150℃ | ||||||
SWANCOR 900 | Temperature resistance up to 165℃ | ||||||
SWANCOR 977-S | Superior performance at extreme temperature up to 210℃ | ||||||
Table 1. Typical Properties of Liquid Resins
PROPERTY | SWANCOR 907-1 | SWANCOR 900 | 0SWANCOR 977-S |
Solid Content, % | 64.567±1 | 55±1 | 71.5±2.0 |
Viscosity, cps*1 | 335±65 | 350±100 | 750±150 |
Specific Gravity | 1.06±0.02 | 1.07±0.01 | 1.08±0.02 |
Shelf Life, months(25℃）*2 | 6 | 6 | 6 |
*1 Brookfield viscometer LVT#3 spindle, 60 rpm at 25℃
*2 Non-promoted and non-thixotroped resin at 25℃
Table 2. Typical Properties of 3.2mm Clear Casting
PROPERTY | SWANCOR 907-1 | SWANCOR 900 | SWANCOR 977-S |
Tensile Strength, psi | 11,000-13,000 | 11,000-13,000 | 9,000-11,000 |
Tensile Modulus, 105 psi | 5.0-5.3 | 5.0-5.3 | 5.2-5.6 |
Tensile Elongation, % | 2.0-4.0 | 2.2-2.8 | 1.5-2.5 |
Flexural Strength, psi | 18,000-21,000 | 17,000-20,000 | 13,000-18,000 |
Flexural Modulus, 105psi | 5.2-5.9 | 5.4-5.9 | 5.6-6.2 |
Volume Shrinkage, % | 8.5-9.5 | 9.0-9.5 | 9.0-10.0 |
Heat Distortion Temperature, ℃*4 | 144-150*3 | 155-165*4 | 205-210*4 |
Barcol Hardness | 40-46 | 40-46 | 45-55 |
*3 Post condition: 24 hours at room temperature then 24 hours at 150℃
*4 Post condition: 24 hours at room temperature then 24 hours at 200℃Table 3. Gel Time Table of SWANCOR 907-1 Using MEKP
Materials | 10-20 min | 20-40 min | 40-60 min | |||||
Cured by MEKP/CoOct/DMA*5 | ||||||||
20℃/64°F | MEKP CoOct DMA | 1.50% 0.40% 0.08% | 1.00% 0.40% 0.08% | 1.00% 0.30% 0.06% | ||||
25℃/77°F | MEKP CoOct DMA | 1.00% 0.30% 0.06% | 1.00% 0.40% 0.08% | 1.00% 0.20% 0.03% | ||||
30℃/86°F | MEKP CoOct DMA | 1.00% 0.30% 0.06% | 1.00% 0.25% 0.04% | 0.90% 0.20% 0.03% | ||||
*5 Concentration: CoOct: 6%, DMA: 100%
Table 4. Gel Time Table of SWANCOR 907-1 Using CHP
Materials | 10-20 min | 20-40 min | 40-60 min | |||||
Cured by CHP/CoOct/DMA*6 | ||||||||
20℃/64°F | CHP CoOct DMA | 1.20% 0.50% 0.08% | 1.00% 0.40% 0.06% | 1.00% 0.20% 0.04% | ||||
25℃/77°F | CHP CoOct DMA | 1.00% 0.40% 0.06% | 1.00% 0.20% 0.04% | 0.80% 0.20% 0.02% | ||||
30℃/86°F | CHP CoOct DMA | 1.00% 0.20% 0.04% | 0.60% 0.20% -- | 0.50% 0.20% -- | ||||
*6 Concentration: CoOct: 6%, DMA: 100%
Table 5. Gel Time Table of SWANCOR 907-1 Using M-50
Materials | 10-20 min | 20-40 min | 40-60 min | |||||
Cured by M-50/CoOct/DMA*7 | ||||||||
20℃/64°F | CoOct DMA M-50 | 0.40% 0.06% 1.00% | 0.30% 0.06% 1.00% | 0.20% 0.05% 1.00% | ||||
25℃/77°F | CoOct DMA M-50 | 0.30% 0.06% 1.00% | 0.25% 0.05% 1.00% | 0.20% 0.05% 1.00% | ||||
30℃/86°F | CoOct DMA M-50 | 0.30% 0.06% 1.00% | 0.30% 0.05% 1.00% | 0.20% 0.02% 0.80% | ||||
*7 Concentration: CoOct: 6%, DMA: 100%
Table 6. Gel Time Table of SWANCOR 900 Using CHP
Materials | 10-20 min | 20-40 min | 40-60 min | |||||
Cured by CHP/CoOct/DMA*8 | ||||||||
20℃/64°F | CHP CoOct DMA | -- -- -- | 3.00% 0.60% 0.10% | 1.50% 0.20% -- | ||||
25℃/77°F | CHP CoOct DMA | 1.50% 0.40% 0.05% | 1.50% 0.20% -- | 1.50% 0.15% -- | ||||
30℃/86°F | CHP CoOct DMA | 1.50% 0.20% 0.02% | 0.80% 0.15% -- | 0.80% 0.10% -- | ||||
*8 Concentration: CoOct: 6%, DMA: 100%
Table 8. Gel Time Table of SWANCOR 977-S Using CHPMaterials | 10-20 min | 20-40 min | 40-60 min | |||||
Cured by CHP/CoOct/DMA*9 | ||||||||
20℃/64°F | CHP CoOct DMA | -- -- -- | 2.00% 0.40% -- | 1.50% 0.20% -- | ||||
25℃/77°F | CHP CoOct DMA | 2.00% 0.40% 0.05% | 1.50% 0.20% -- | 1.50% 0.10% -- | ||||
30℃/86°F | CHP CoOct DMA | 2.00% 0.20% -- | 1.00% 0.15% -- | 1.00% 0.10% -- | ||||
*9 Concentration: CHP: 80%, CoOct: 6%, DMA: 100%