Product name | 302 stainless steel sheet |
Size | Thickness:hot rolled 3mm-160mm/cold rolled 0.1mm - 6mm |
Length:2000mm,2440mm,3000mm,5800mm,6000mm,etc | |
Width:1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,3000mm,3500mm,etc | |
Standard | JIS/SUS/GB/DIN/ASTM/AISI/EN |
Technology | Hot rolled,cold rolled |
Surface | 2B,2D,BA,NO.1,NO.4,NO.8,8K,mirror,checkered,embossed,hairline,sandblast,Brush,etching,etc |
Price terms | FOB, EXW, CIF, CFR,DDP |
Payment terms | 30% Advance payment,70% pay the balance before delivery |
Packing | Standard sea-worthy export packing or customer's request |
Advantage | 1. High strength after cold processing 2. No corrosion, pitting, rust or wear 3. Good corrosion resistance 4. High mechanical strength and extensibility |
Product name | Stainless steel plate cold-rolled 2B (coil, plate) | Stainless steel plate hot rolled No.1 (coil, plate) |
Thickness | 0.1-6.0mm | 3-159mm |
Surface | 2B smooth, BA; 8K mirror; Drawing, grinding; Snowflake sand; Stainless steel no fingerprint plate | 8K mirror; Drawing, titanium plating, matte; Snowflake sand; Stainless steel no fingerprint plate |
302 Stainless steel chemical composition table | ||||||||||||||||
Chemical composition | C | Si | Mn | Cr | Ni | P | S | N | ||||||||
Content(%) | ≤0.15 | ≤1.0 | ≤2.0 | 17.00-19.00 | 8.00-10.00 | ≤0.045 | ≤0.030 | ≤0.10 |
302 stainless steel performance | ||||||||||||||||
Density (20℃)/kg/dm3 | Melting point /℃ | Specific heat capacity (0~100℃)/kg/(kg.k) | Thermal conductivity /w/(m.k)100℃ | Thermal conductivity /w/(m.k)500℃ | Linear expansion coefficient (10-6/k)0~100℃ | Linear expansion coefficient /(10-6/k)0~504℃ | Resistivity (20℃) (ω.mm2 /m) | Longitudinal elastic modulus (20℃) /GPa | ||||||||
7.93 | 1398~1120 | 0.5 | 16.3 | 21.5 | 17.3 | 18.7 | 0.73 | 193 |
302 Stainless steel physical properties table | ||||||||
Tensile strength | Yield strength | Elongation | Shrinkage of section | Hardness | ||||
≥520MPa | ≥205MPa | ≥40% | ≥60% | ≤187HB;≤90HRB;≤200HV |