Cu93P copper brazing alloy phosphorous

Trade Mark

Melting Temp

Working Temp

Tensile Strength(M.pa)

Equal to

Application

As Usual

AWS

A5.8

B-Cu93P

710-800

810-900

470.4

HL201

BCuP-2

Filler metal can be use alone.High level of fluidity,can be use for thin joint gap,brittle filler metal,for brazing copper and brass parts that without impact load.

B-Cu86SnP

620-670

700-780

Low temperature brazing,good fluidity.Easy brazing operation.Brittle filler metal,should use with silver brazing flux for brazing copper and brass parts that without impact load.

B-Cu91PAg

645-790

750-810

HL209/2B

BCuP-6

Can be use for brazing big joint gap in low temperature.High fluidity in high temperature.Use with silver brazing flux for brazing copper and copper alloy. 

B-Cu88PAg

645-771

750-860

HL205/5B

BCuP-7

Use with silver brazing flux for brazing copper and copper alloy that high strength required,especially foe brazing copper tubing in airconditions,freezers,refrigerators and electric motor's conductors.

B-Cu89PAg

645-815

820-860

519

5B-1

BCuP-3

Similar with above.

B-Cu80PAg

640-815

810-850

499.8

HL204/15B

BCuP-5

Low temperature brazing ,good fluidity.Use with silver brazing paste suitable for high strength required copper and copper alloy parts.